Cemented carbide electrode, also known as YD type cemented carbide composite electrode (referred to as YD type welding electrode, commonly known as mace) is made of sintered sintered cemented carbide and elastic matrix alloy. Sintered carbide particles are mainly diamond-containing tungsten carbide, and its hardness can reach 89-91HRA. The body metal is generally "nickel-copper" alloy, the bending strength is about 690Mpa, and the hardness is ≥160HB. The carbide composite electrode needs to be used in conjunction with a substrate flux.
It is mainly used to overlay the worn-out and cutting usage workpieces in oil, mining, coalmining, geology, construction and other industries.Such as: milling shoes, wear shoescentralizers, reamer, drill pipe joints, hydraulic cutter, scraper blade plow planer, drill corepiling drill.auger, etc.The oxyacetylene butt, the operating process is as follows:
(1) clean up the workpiece, make the welding workpieces surface with metallic luster.
(2) the flat position of welding, therefore can use the appropriate clamping fixture for control of surfacing layer thickness, thick piece of available.
(3) with a neutral flame preheating, flame core not contact surface, the distance to 25 mm is advisable.
(4) carbide surfacing welding layer.With YD type electrode surfacing, the use of neutral flame (can be slightly carbonizing flame) tip is steady on the workpiece surface movement, the flame of the alloy electrode heating (be careful not to make flame cone tip contact alloy particles), tire body in the electrode alloy melt, carbide particles are also falling.Before the tire body of molten metal solidification, the particles arrange, can use left hand of the alloy electrode fingers, or another person holding a base electrode or pull rod on graphite rod in a quick stir particles, making them evenly aligned neatly.Surfacing layer thickness control according to the requirements of design.
(5) after the workpiece welding, where no ventilation, slow cooling, cannot quench, conditional usable asbestos blanket cover.
(6) the workpiece after cooling to room temperature, if necessary, grinding surface surfacing to required size and shape.
(7) clean up the workpiece, remove all splash, slag, etc.
Compositions:
Grade | Black Silicon Caride Grits | Ni/Ag (Cu) |
ZZT21 | 60-70% | 30-40% |
Rods length (mm) | 280/350/450/450 |
Rods diameter (mm) | 12/12/16/22 |
Black Silicon Carbide Grits Size (mm) | 1.6-3.2 |
3.2-4.8 | |
4.8-6.4 | |
6.4-8 | |
8-9.5 |